| Is It ISO Certified | ISO Certified |
| Form | Plates |
| Sizes | As Per Requirement |
| Material Grade | Monel 400,UNS N04400,Monel K500,UNS N05500,Monel R405,UNS N04405 |
| Color | Silver |
| Material | Monel |
| Type | Plates |
| Test Certificate | Available |
| Steel Grade | SS 304, 304L, 304LN, 309, 309S, 310, 316, 316H, 316L, 321, 321H, 347, 347H, 348, 348H |
| Standard | ASTM, AISI |
| Thickness | Or As Per Requirement, >5 mm, 4-5 mm, 3-4 mm, 2-3 mm, 1-2 mm, 0-1 mm |
| Surface Treatment | Coated, Hot Rolled, Painted |
| Condition | New |
| Certification | ISO |
| Type | Plate |
| Place Of Origin | India |
| Is It Rust Proof | Non Rust Proof |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Size | As Per Requirement |
| Certification | ISO |
| I Deal In | New Only |
| Length | As Per Requirement |
| Packing Details | Shrink Wrapping, Jute Wrapping, Bubble Wrapping, Wooden Boxes or As Per Requirement |
| Element | % |
| C | 0.17 |
| Mn | 1.6 |
| P | 0.035 |
| S | 0.015 |
| Si | 0.35 |
| Cr | 0.25 |
| V | 0.11 |
| Cu | 0.35 |
| N | 0.030 |
| Nb | 0.050 |
| Al | 0.06 |
| Properties | |
| Density (×1000 kg/m3) | 7.7-8.03 |
| Poisson's Ratio | 0.27-0.30 |
| Elastic Modulus (GPa) | 190-210 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Size | As Per Requirement |
| Usage/Application | Industrial & Construction |
| Certification | ISO |
| I Deal In | New Only |
| Length | As Per Requirement |
| Element | % |
| C | 0.2 |
| Si | 0.13-0.60 |
| Mn | 0.84-1.72 |
| P | 0.030 |
| S | 0.030 |
| Cu | ≤0.38 |
| Ni | ≤0.63 |
| Cr | ≤0.34 |
| Mo | ≤0.33 |
| V | ≤0.08 |
| Co | ≤0.05 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 65-100 | 415 | 585-705 | 20% |
| 100 | 415 | 585-705 | 20% |
| 06-65 | 415 | 585-705 | 20% |
| Finish | Unpolished, Polished |
| Packaging Type | Coils |
| Size | As Per Requirement |
| Grade | 300 series, 600 series, 500 series, 200 series, 400 series |
| Material | Stainless Steel |
| Product Type | Coils |
| Condition | New |
| Condition | New |
| Customisation | Customised |
| Material | Stainless Steel, Alloy Steel, Carbon Steel, Mild Steel |
| Is It Anodised | Anodised |
| Certification | Available |
| Size | As Per Requirement |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.12 - 0.2 |
| Si | max 0.35 |
| Mn | 0.4 - 0.9 |
| Ni | max 0.3 |
| P | max 0.025 |
| S | max 0.01 |
| Cr | max 0.3 |
| Mo | 0.25 - 0.35 |
| N | max 0.012 |
| Cu | max 0.3 |
| Thickness | >5 mm, 0-1 mm, 4-5 mm, 3-4 mm, 2-3 mm, 1-2 mm |
| Grade | SS 304H |
| Material | SS |
| Standards | ANSI/ASME B16.11 & BS3799 |
| Finishing | Powder Coated, Painted |
| Element | % |
| C | 0.18-0.25 |
| Si | 0.20-0.40 |
| Mn | 0.40-0.70 |
| P | 0.030 |
| S | 0.030 |
| Cr | ≤ 0.30 |
| Mo | 0.30-0.40 |
| Size | As Per Requirement |
| Grade | 1.5015, G8Mn7 |
| Element | % |
| C | 0.06-0.10 |
| Si | 0.60 |
| Mn | 1.50-1.80 |
| P | 0.020 |
| S | 0.015 |
| Nb | ≤0.05 |
| V | ≤ 0.10 |
| N | ≤ 0.02 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.35 - 0.42 |
| Si | 1.5 - 1.8 |
| Mn | 0.5 - 0.8 |
| P | max 0.025 |
| S | max 0.025 |
| - | Cu 10Sn < 0.6 |
| Thickness | 1-2 mm, 2-3 mm, 0-1 mm, >5 mm, 3-4 mm, 4-5 mm |
| Element | % |
| C | 0.42 - 0.50 |
| Si | 1.5 - 2.0 |
| Mn | 0.5 - 0.8 |
| P | max 0.025 |
| S | max 0.025 |
| - | Cu 10Sn < 0.6 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.47 - 0.55 |
| Si | 1.50 - 1.80 |
| Mn | 0.50 - 0.80 |
| P | 0.045 |
| S | 0.045 |
| Cr | - |
| Mo | - |
| others | N 0.007 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.68 - 0.75 |
| Si | 1.50 - 1.80 |
| Mn | 0.60 - 0.80 |
| P | 0.035 |
| S | 0.035 |
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.7-0.11 |
| Si | 0.55-0.75 |
| Mn | 1.03-1.27 |
| P | 0.20 |
| S | 0.20 |
| Cr | 0.12 |
| Mo | 0.12 |
| Ni | 0.12 |
| Al | 0.20 |
| Cu | 0.17 |
| Ti Zr | 0.13 |
| Thickness | 1-2 mm, 0-1 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
We are:
1.5113 - 8MnSi7 Plate Stockist
1.5113 - 8MnSi7 Plate Supplier
1.5113 - 8MnSi7 Plate Trader
1.5113 - 8MnSi7 Plate Dealer
1.5113 - 8MnSi7 Plate Manufacturer
1.5113 - 8MnSi7 Plate Exporter
| Element | % |
| C | max 0.1 |
| Si | 0.9 - 1.1 |
| Mn | 1.6 - 1.8 |
| P | max 0.025 |
| S | max 0.025 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.34 - 0.42 |
| Si | 0.70-0.90 |
| Mn | 0.90-1.20 |
| P | 0.035 |
| S | 0.035 |
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.42-0.50 |
| Si | 0.70-0.90 |
| Mn | 0.90-1.20 |
| P | 0.035 |
| S | 0.035 |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.45 - 0.53 |
| Si | 0.70 - 1.10 |
| Mn | 90 - 1.20 |
| P | 0.035 |
| S | 0.035 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.18-0.25 |
| Si | 0.20-0.40 |
| Mn | 0.40-0.70 |
| P | 0.030 |
| S | 0.030 |
| Cr | ≤ 0.30 |
| Mo | 0.30-0.40 |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.38 - 0.45 |
| Si | 0.15 - 0.35 |
| Mn | 1.60 - 1.90 |
| P | 0.35 |
| S | 0.35 |
| V | 0.7 - 0.12 |
| Thickness | 0-1 mm, 1-2 mm, 4-5 mm, 2-3 mm, 3-4 mm, >5 mm |
| Element | % |
| C | max 0.18 |
| Si | max 0.4 |
| Mn | 0.9 - 1.4 |
| P | max 0.025 |
| S | max 0.015 |
| Mo | 0.4 - 0.6 |
| V | 0.04 - 0.08 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | ≤0.19 |
| Si | 0.20 - 0.50 |
| Mn | 1.40 - 1.70 |
| P | 0.035 |
| S | 0.035 |
| Cr | - |
| Mo | 0.20 - 0.50 |
| Ni | ≤1.00 |
| Others | V ≤0.19N≤0.020 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.17 - 0.25 |
| Si | 0.15 - 0.35 |
| Mn | 0.50 - 0.80 |
| P | 0.035 |
| S | 0.035 |
| Cr | 0.20 - 0.40 |
| Mo | 0.45 - 0.55 |
| Ni | ≤0.30 |
| Others | V 0.25 - 0.35 |
| Thickness | 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm |
| Element | % |
| C | max 0.2 |
| Si | max 0.4 |
| Mn | 0.9 - 1.5 |
| Ni | max 0.3 |
| P | max 0.015 |
| S | max 0.005 |
| Cr | max 0.3 |
| Mo | 0.45 - 0.6 |
| N | max 0.012 |
| Cu | max 0.3 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.22 - 0.29 |
| Si | max 0.4 |
| Mn | max 1.5 |
| Ni | max 0.4 |
| P | max 0.025 |
| S | max 0.035 |
| Mo | 0.15 - 0.25 |
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.35 - 0.4 |
| Si | max 0.3 |
| Mn | 0.6 - 0.9 |
| P | max 0.025 |
| S | max 0.025 |
| Mo | 0.2 - 0.3 |
| Cu | max 0.25 |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.15 - 0.23 |
| Si | max 0.6 |
| Mn | 0.5 - 1 |
| Ni | max 0.4 |
| P | max 0.025 |
| S | max 0.02 |
| Cr | max 0.3 |
| Mo | 0.4 - 0.6 |
| V | max 0.05 |
| Cu | max 0.3 |
*Your information is safe with us.
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Element | % |
| C | 0.15 - 0.2 |
| Si | max 0.6 |
| Mn | 0.8 - 1.2 |
| Ni | max 0.4 |
| P | max 0.02 |
| S | max 0.02 |
| Cr | max 0.3 |
| Mo | 0.45 - 0.65 |
| V | max 0.05 |
| Cu | max 0.3 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.06-0.10 |
| Si | 0.6 |
| Mn | 1.50-1.80 |
| P | 0.020 |
| S | 0.015 |
| Cr | ≤ 0.20 |
| Mo | 0.30-0.40 |
| Thickness | 4-5 mm, 2-3 mm, 3-4 mm, 1-2 mm, >5 mm, 0-1 mm |
| Element | % |
| C | 0.06 - 0.1 |
| Si | 0.1 - 0.35 |
| Mn | 0.6 - 0.8 |
| P | max 0.025 |
| S | max 0.01 |
| Cr | max 0.2 |
| Mo | 0.4 - 0.5 |
| Ti | max 0.06 |
| Al | max 0.06 |
| Cu | max 0.3 |
| B | 0.002 - 0.006 |
*Your information is safe with us.
| Thickness | 2-3 mm, >5 mm, 1-2 mm, 3-4 mm, 4-5 mm, 0-1 mm |
| Element | % |
| C | 0.17 |
| Si | 0.15-0.40 |
| Mn | 0.9 |
| P | 0.035 |
| S | 0.04 |
| Cu (min) | 0.20 |
| Thickness | Yield | Tensile | Elongation |
| mm | Min Mpa | Mpa | Min % |
| t50 | 345-450 | 185 | 28 |
| 50 | 345-450 | 185 | 25 |
| Thickness | 1-2 mm, 2-3 mm, 0-1 mm, 4-5 mm, >5 mm, 3-4 mm |
| Element | % |
| C | 0.05-0.17 |
| Mn | 0.40-0.65 |
| P | 0.025 |
| S | 0.025 |
| Si | 0.50-0.80 |
| Cr | 1.00-1.50 |
| Mo | 0.45-0.65 |
| V | - |
| Tensile (MPa) | Yield (MPa) | Elong. (50mm) |
| 515 - 690 | 310 min | 22% min |
| Thickness | 0-1 mm, 4-5 mm, 2-3 mm, 3-4 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.22 |
| Si | 0.15-0.50 |
| Mn | 1.15-1.50 |
| P | 0.035 |
| S | 0.04 |
| N | 0.01-0.03 |
| V | 0.04-0.11 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.18 |
| Si | 0.6 |
| Mn | 1.65 |
| P | 0.025 |
| S | 0.035 |
| V | 0.08 |
| Ni | 0.020 |
| Co | 0.10 |
| Thickness | 4-5 mm, 2-3 mm, 1-2 mm, 0-1 mm, >5 mm, 3-4 mm |
| Element | % |
| C | 0.18 |
| Si | 0.6 |
| Mn | 1.65 |
| P | 0.025 |
| S | 0.035 |
| V | 0.08 |
| Ni | 0.020 |
| Co | 0.10 |
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Element | % |
| C | 0.08 |
| Mn | 0.95-1.50 |
| P | 0.015 |
| S | 0.006 |
| Si | 0.15-0.35 |
| Cu | 0.90-1.20 |
| Ni | 0.65-1.00 |
| Cr | 0.40-0.65 |
| Mo | 0.40-0.65 |
| V | 0.04 - 0.08 |
| Al | 0.02 - 0.05 |
| Ni | 0.015 |
| Nb | 0.01-0.03 |
| Yield strength (min) | 100 ksi (690 Mpa) |
| Tensile strength | 110-130 ksi (760-895 Mpa) |
| Elongation in 2" (50 mm)min | 18% |
*Your information is safe with us.
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.20 |
| Mn | 1.15-1.50 |
| P | 0.035 |
| S | 0.03 |
| Si | 0.15-0.50 |
| Nb | 0.05 |
| Properties | |
| Density (×1000 kg/m3) | 7.7-8.03 |
| Poisson's Ratio | 0.27-0.30 |
| Elastic Modulus (GPa) | 190-210 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.20 |
| Mn | 1.15-1.50 |
| P | 0.035 |
| S | 0.03 |
| Si | 0.15-0.50 |
| V | 0.04-0.11 |
| N | 0.03 |
| Properties | |
| Density (×1000 kg/m3) | 7.7-8.03 |
| Poisson's Ratio | 0.27-0.30 |
| Elastic Modulus (GPa) | 190-210 |
| Thickness | 4-5 mm, 0-1 mm, 3-4 mm, 1-2 mm, 2-3 mm, >5 mm |
| Element | (%) |
| C | 0.190 - 0.250 |
| Mn | 1.35 - 1.65 |
| S | 0.05 |
| P | 0.04 |
| Fe | 98.01 - 98.46 |
*Your information is safe with us.
| Thickness | 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm |
| Element | % |
| C | ≤0.10 |
| Mn | 1.1-1.65 |
| P | ≤0.025 |
| S | ≤0.01 |
| Si | 0.1-0.50 |
| Ni | ≤0.40 |
| Cr | ≤0.20 |
| Mo | ≤0.06 |
| Cu | ≤0.35 |
| V | ≤0.10 |
| Nb | ≤0.05 |
| Al | ≤0.08 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 5t≤300 | 450 | 540-690 | 18 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| Ni | Balance |
| Fe | 0.40 max |
| C | 0.15 max |
| Mn | 0.35 max |
| Si | 0.35 max |
| Cu | 0.25 max |
| S | 0.01 max |
| Applications of ASTM B162 Plates |
| Electronic Industries |
| Chemical Industries |
| Soap Industries |
| Aerospace Industries |
| Food Industries |
| Fabrication Industries |
| Tensile Strength min, psi | annealed | 55,000 |
| Yield (0.2% offset) min, psi | annealed | 15,000 |
| Elongation | annealed | 40 |