| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Size | As Per Requirement |
| Certification | ISO |
| Length | As Per Requirement |
| I Deal In | New Only |
| Packing Details | Shrink Wrapping, Jute Wrapping, Bubble Wrapping, Wooden Boxes or As Per Requirement |
| Element | % |
| C | 0.17 |
| Si | 0.08-0.45 |
| Mn | 0.98 |
| P | 0.035 |
| S | 0.035 |
| Thickness | Yield | Tensile | Elongation |
| mm | Min Mpa | Mpa | Min % |
| 06-50 | 165 | 310-450 | 30% |
| 50-200 | 165 | 310-450 | 27% |
| Steel Grade | A515 |
| Standard | ASTM |
| Thickness mm | 200- 50 |
| Elongation Min % | 21, 25 |
| Tensile Mpa | 415-550 |
| Yield Min Mpa | 220 |
| Element | % |
| C | 0.24-0.31 |
| Mn | 0.98 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.13-0.45 |
| Nominal Size | 1/2 inch, 3/4 inch, 1 inch, 2 inch, 3 inch, >3 inch |
| Length | 3m, 6m, 12m, 18m, 24m, >24m |
| Shape | Round |
| Surface Finish | Anodized, Brushed, Mill Finished, Finished Polished, Sand Blasted |
| Alloy Or Not | Iss Alloy |
| Element | % |
| C | 0.23 |
| Cr | 1.2 - 1.8 |
| Fe | 94.75 |
| Mn | 0.40 |
| Ni | 2.25 - 3.25 |
| P | 0.020 |
| Si | 0.20 - 0.40 |
| S | 0.020 |
| V | 0.030 |
*Your information is safe with us.
| Shape | Round |
| Size | 0-1 inch, 1-2 inch, 2-3 inch, 3-4 inch, > 4 inch |
| Material Grade | ASTM A299 Grade A |
| Unit Length | 6 m, 12 m, 18 m, 24m |
| Element | % |
| C (max) | 0.28-0.30 |
| Si (max) | 0.13-0.45 |
| Mn | 0.84 -1.62 |
| P (max) | 0.035 |
| S (max) | 0.035 |
| Thickness | Yield strength (Mpa) | Tensile strength (Mpa) | Elongation ≥,% 200mm |
| T≤25 | 325 | 550-690 | 16 |
| T>25 | 310 |
| Thickness | 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm |
| Element | % |
| C | 0.18-0.25 |
| Si | 0.13-0.45 |
| Mn | 0.90-0.98 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 65-85 [450-585] |
| Yield strength, min, kis [MPa] | 37 [255] |
| Elongation in 8 in. [200 mm], min, % | 19 |
| Elongation in 2 in. [50 mm], min, % | 23 |
| Thickness | 4-5 mm, 0-1 mm, >5mm, 2-3 mm, 3-4 mm, 1-2 mm |
| Surface Treatment | Coated, Painted, Cold Rolled |
| Type | Plate |
| Element | % |
| C | 0.20-0.27 |
| Si | 0.13-0.45 |
| Mn | 0.90-0.98 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 70-90 [485-620] |
| Yield strength, min, kis [MPa] | 40 [275 |
| Elongation in 8 in. [200 mm], min, % | 17 |
| Elongation in 2 in. [50 mm], min, % | 21 |
*Your information is safe with us.
| Thickness | 3-4 mm, 0-1 mm, 2-3 mm, 4-5 mm, >5 mm, 1-2 mm |
| Standard | ASTM |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Element | % |
| C max | 0.18 |
| Si max | 0.5 |
| Mn | 0.90-1.60 |
| P max | 0.035 |
| S max | 0.035 |
| Als min | 0.015 |
| Ti max | 0.02 |
| Cu max | 0.35 |
| Cr max | 0.2 |
| Ni max | 0.4 |
| Mo max | 0.08 |
| Nb | 0.02-0.05 |
| V | 0.05-0.10 |
| Standard | ASTM |
| Thickness | 4-5 mm, >5 mm, 3-4 mm, 0-1 mm, 1-2 mm, 2-3 mm |
| Element | % |
| C | 0.23-0.28 |
| Si | 0.13-0.45 |
| Mn | 0.90-0.98 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 75-95 [515-655] |
| Yield strength, min, kis [MPa] | 43 [295] |
| Elongation in 8 in. [200 mm], min, % | 16 |
| Elongation in 2 in. [50 mm], min, % | 20 |
| Thickness | 0-1 mm, 1-2 mm,2-3 mm,3-4 mm,>5 mm, 4-5 mm |
| Element | % |
| C | 0.24 |
| Si | 0.15-0.40 |
| Mn | 0.9 |
| P | 0.035 |
| S | 0.04 |
| Cu (min) | 0.2 |
| Tensile strength, kis [MPa] | 55-75 [380-515] |
| Yield strength, min, kis [MPa] | 30 [205] |
| Elongation in 8 in. [200 mm], min, % | 22 |
| Elongation in 2 in. [50 mm], min, % | 25 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.27 |
| Si | 0.15-0.40 |
| Mn | 0.9 |
| P | 0.035 |
| S | 0.04 |
| Cu (min) | 0.2 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| t≤50 | 415-550 | 230 | 23 |
| 50 | 415-550 | 230 | 20 |
| Thickness | >5 mm, 0-1 mm, 1-2 mm, 4-5 mm, 2-3 mm, 3-4 mm |
| Element | % |
| C | 0.22 |
| Si | 0.08-0.45 |
| Mn | 0.98 |
| P | 0.035 |
| Si | 0.035 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-50 | 185 | 345-485 | 28% |
| 50-200 | 185 | 345-485 | 25% |
| Thickness | >5 mm, 1-2 mm, 3-4 mm, 4-5 mm, 0-1 mm, 2-3 mm |
| Element | % |
| C | 0.16 |
| Si | 0.35 |
| Mn | 0.4/1.2 |
| P | 0.03 |
| S | 0.03 |
| Al | 0.02 |
| Cr | 0.3 |
| Cu | 0.3 |
| Ni | 0.3 |
| Mo | 0.08 |
| Nb | 0.01 |
| Ti | 0.03 |
| V | 0.02 |
| Tensile N/mm² | Yield/min N/mm² |
| 360/480 | 235 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.28-0.30 |
| Si | 0.13-0.45 |
| Mn | 0.84 -1.62 |
| P | 0.035 |
| S | 0.035 |
| Thickness mm | Yield Strength Min Mpa | Tensile Strength Mpa | Elongation Min % |
| 5≤t≤50 | 310-325 | 550-690 | 19% |
| 50≤t≤100 | 310-325 | 550-690 | 19% |
| Thickness | 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm |
| Element | % |
| C max | 0.15 |
| Mn | 2.00 |
| S | 0.03 |
| N | - |
| Cu | 0.30 |
| Si | 1.00 |
| P | 0.045 |
| Cr | 17/19 |
| Ni | 8/10 |
| Mo | - |
| Yield Strength [MPa] | Tensile Strength [MPa] |
| 345 | 550 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C max | 0.15 |
| Mn | 2.00 |
| S | 0.03 |
| N | - |
| Cu | 0.30 |
| Si | 1.00 |
| P | 0.045 |
| Cr | 17/19 |
| Ni | 8/10 |
| Mo | - |
| Yield Strength [MPa] | Tensile Strength [MPa] |
| 345 | 550 |
*Your information is safe with us.
| Thickness | 2-3 mm, 3-4 mm, 1-2 mm, >5 mm, 0-1 mm, 4-5 mm |
| Element | % |
| C | 0.20-0.25 |
| Si | 0.13–0.45 |
| Mn | 1.07-1.62 |
| P | 0,035 |
| S | 0,035 |
| Ni | 0.67-1.03 |
| Mo | 0.41–0.64 |
| Thickness | Yield | Tensile Strength | Elongation |
| Strength | |||
| mm | Min Mpa | Mpa | Min % |
| 5≤t≤50 | 345 | 550-690 | 20% |
| 50≤t≤200 | 345 | 550-690 | 17% |
| Thickness | 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm |
| Element | % |
| C | 0.13 |
| Mn | 0.9 |
| P | 0.035 |
| S | 0.040 |
| Si | 0.15-0.30 |
| Ni | 8.50-9.50 |
| Thickness mm | Yield Min Mpa | Elongation Min % |
| 5 < t30 | 585-820 | 18 |
| 30 < t | 575-820 | 18 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.05-0.21 |
| Mn | 0.55-0.80 |
| P | 0.025 |
| S | 0.025 |
| Si | 0.15-0.40 |
| Cr | 0.50-0.80 |
| Mo | 0.45-0.60 |
| V | - |
| Tensile (MPa) | Yield (MPa) | Elong. (50 mm) |
| 380 - 550 | 230 min | 22% min |
*Your information is safe with us.
| Thickness | 1-2 mm, 4-5 mm, >5 mm, 3-4 mm, 0-1 mm, 2-3 mm |
| Element | Max % |
| C | 0.18 |
| Si | 0.4 |
| Mn | 0.50-1.40 |
| P | 0.03 |
| S | 0.03 |
| AL | 0.02 |
| Cr | 0.3 |
| Cu | 0.3 |
| Mo | 0.08 |
| N | 0.02 |
| Nb | 0.05 |
| Ni | 0.5 |
| Ti | 0.03 |
| V | 0.05 |
| Nb Ti V | 0.05 |
| Thickness (mm) | Yield Strength MPa (min) | Tensile Strength Mpa | Elongation % (min) |
| ≤ 16 | 275 | ||
| 16 > to ≤35 | 275 | ||
| 35 > to ≤50 | 265 | ||
| 50 > to ≤70 | 255 | 370-490 | 23 |
| 70 > to ≤100 | 235 | 350-470 | 1) |
| 100 > to ≤150 | 225 | 1) | 1) |
| >150 | 390-510 | 24 |
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Element | % |
| C | 0.14-0.21 |
| Mn | 0.95-1.30 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.15-0.35 |
| Ni | 1.20-1.50 |
| Cr | 1.00-1.50 |
| Mo | 0.40-0.60 |
| V | 0.03-0.08 |
| Ti | - |
| Zr | - |
| Cu | - |
| B | - |
| Nb | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
| Thickness | 1-2 mm, 2-3 mm, >5 mm, 0-1 mm, 4-5 mm, 3-4 mm |
| Element | % |
| C | 0.10-0.20 |
| Mn | 0.60-1.00 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.15-0.35 |
| Ni | 0.70-1.00 |
| Cr | 0.40-0.65 |
| Mo | 0.40-0.60 |
| V | 0.03-0.08 |
| Ti | - |
| Zr | - |
| Cu | 0.15-0.50 |
| B | 0.001-0.005 |
| Nb | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.12-0.21 |
| Mn | 0.95-1.30 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.20-0.35 |
| Ni | 0.30-0.70 |
| Cr | 0.40-0.65 |
| Mo | 0.20-0.30 |
| V | 0.03-0.08 |
| Ti | - |
| Zr | - |
| Cu | - |
| B | 0.001-0.005 |
| Nb | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.12-0.21 |
| Mn | 0.45-0.70 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.20-0.35 |
| Ni | 1.20-1.50 |
| Cr | 0.85-1.20 |
| Mo | 0.45-0.60 |
| V | - |
| Ti | - |
| Zr | - |
| Cu | - |
| B | 0.001-0.005 |
| Nb | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
| Thickness | 4-5 mm, >5 mm, 1-2 mm, 2-3 mm, 3-4 mm |
| Surface treatment | Painted,hot Rolled |
| Element | % |
| C | 0.11-0.21 |
| Mn | 1.10-1.50 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.15-0.45 |
| Ni | - |
| Cr | - |
| Mo | 0.10-0.60 |
| V | 0.06 |
| Ti | - |
| Zr | - |
| Cu | - |
| B | 0.001-0.005 |
| Nb | 0.06 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.08-0.22 |
| Si | 0.13-0.37 |
| Mn | 0.55-1.10 |
| P | 0.035 |
| S | 0.035 |
| Cr | 0.36-0.69 |
| Mo | 0.36-0.64 |
| B | 0.0005-0.006 |
| V | 0.02-0.09 |
| Ni | 0.67-1.03 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-65 | 690 | 795-930 | 16% |
| 65-150 | 620 | 725-930 | 14% |
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.10-0.23 |
| Si | 0.13-0.37 |
| Mn | 0.87-1.41 |
| P | 0.035 |
| S | 0.035 |
| Ni | 0.27-0.73 |
| Cr | 0.36-0.69 |
| Mo | 0.17-0.33 |
| B | ≥0.0005 |
| V | 0.02-0.09 |
| Cu | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-65 | 690 | 795-930 | 16% |
| 65-150 | 620 | 725-930 | 14% |
| Thickness | >5 mm, 0-1 mm, 4-5 mm, 2-3 mm, 3-4 mm, 1-2 mm |
| Element | % |
| C | 0.12-0.23 |
| Mn | 0.87-1.41 |
| P | 0.035 |
| S | 0.035 |
| SI | 0.13-0.37 |
| Ni | 1.15-1.55 |
| Cr | 0.94-1.56 |
| Mo | 0.36-0.64 |
| V | 0.02-0.09 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.27 |
| Si | 0.04 |
| Mn | 1.35 |
| P | 0.05 |
| S | 0.4 |
| Cu | 0.2 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | ≤0.27 |
| Mn | ≤1.35 |
| P | ≤0.04 |
| S | ≤0.05 |
| Si | ≤0.40 |
| Cu | ≥0.20 |
| Ni |
| Thickness | Yield | Tensile | Elongation |
| Strength | Strength | ||
| mm | Min Mpa | Mpa | Min % |
| 5t≤300 | 380 | 485-690 | 17% |
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.24 |
| Si | 0.13–0.55 |
| Mn | 0.64-1.46 |
| P | 0,035 |
| S | 0,035 |
| Cu | 0.38 |
| Cr | 0.29 |
| Ni | 0.28 |
| Mo | 0.09 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-65 | 415 | 550-690 | 22% |
| 65-100 | 380 | 515-655 | 20% |
*Your information is safe with us.
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.24 |
| Si | 0.13–0.55 |
| Mn | 0.64-1.46 |
| P | 0,035 |
| S | 0,035 |
| Cu | 0.38 |
| Cr | 0.29 |
| Ni | 0.28 |
| Mo | 0.09 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-65 | 380 | 550-690 | 22% |
| 65-100 | 345 | 515-655 | 20% |
| 100-150 | 275 | 485-620 |
| Thickness | 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm |
| Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | |
| ≤ 40 mm | > 40 mm | |||||||||
| A537 Class 1 | 0.24 | 0.15/0.50 | 0.70/1.35 | 1.00/1.60 | 0.035 | 0.035 | 0.25 | 0.8 | 0.25 | 0.35 |
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Tensile strength ksi (Mpa) | 105-125 (725-860) |
| Yield strength , Min , ksi (Mpa) | 85 (585) |
| Elongation 2in (50mm) ,%, A | 14 |
*Your information is safe with us.
| Thickness | >5 mm, 1-2 mm, 0-1 mm, 2-3 mm, 4-5 mm, 3-4 mm |
| Element | % |
| C | 0.2 |
| Si | 0.15-0.50 |
| Mn | 0.70-1.35 |
| P | 0.035 |
| S | 0.04 |
| Cr | 0.25 |
| Cu | 0.35 |
| Mo | 0.08 |
| Ni | 0.25 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.18 |
| Si | 0.5 |
| Mn | 0.9/1.60 |
| P | 0.035 |
| S | 0.035 |
| Al acid | ≥ 0.015 |
| Nb | 0.02/0.05 |
| V | 0.03/0.10 |
| Ti | 0.02 |
| Ni | 0.4 |
| Cu | 0.35 |
| Cr | 0.2 |
| Mo | 0.08 |
| N | - |
| Yield strength (Mpa) | Tensile strength (Mpa) | Impacting Test |
| temperature (℃) | ||
| ≥390 | 510-650 | 0 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.15 |
| Mn | 0.30-0.60 |
| P | 0.025 |
| S | 0.025 |
| Si | 0.50 |
| Cr | 4.00-6.00 |
| Mo | 0.45-0.65 |
| V | - |
| Tensile (MPa) | Yield (MPa) | Elong. (50mm) |
| 415 - 585 | 205 min | 18% min |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.17 |
| Si | 0.13-0.45 |
| Mn | 0.70-0.80 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 65-85 [450-585] |
| Yield strength, min, kis [MPa] | 37 [255] |
| Elongation in 8 in. [200 mm], min, % | 19 |
| Elongation in 2 in. [50 mm], min, % | 23 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.20-0.25 |
| Si | 0.13–0.45 |
| Mn | 1.07-1.62 |
| P | 0,035 |
| S | 0,035 |
| Ni | 0.37-0.73 |
| Mo | 0.41–0.64 |
| Thickness | Yield | Tensile Strength | Elongation |
| Strength | |||
| mm | Min Mpa | Mpa | Min % |
| 5≤t≤50 | 345 | 550-690 | 20% |
| 50≤t≤200 | 345 | 550-690 | 17% |
| Standard | ASTM |
| Shape | Rectangular |
| Material | SS |
| Element | % |
| C | 0.25 |
| Mn | 1.15/1.50 |
| P | 0.035 |
| S | 0.035 |
| Si | 015/0.40 |
| Mo | 0.45/0.60 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Surface Treatment | Coated, Painted, Hot Rolled |