Aesteiron Steels LLP
Girgaon, Mumbai, Maharashtra
Send SMS
Send E-mail
| Thickness | 0-1 mm, 4-5 mm, >5 mm |
| Size | As Per Requirement |
| Certification | ISO |
| I Deal In | New Only |
| Packing Details | Shrink Wrapping, Jute Wrapping, Bubble Wrapping, Wooden Boxes or As Per Requirement |
| Usage/Application | Industrial & Construction |
| Element | % |
| C | 0.03-0.09 |
| Mn | 0.45-1.3 |
| P | ≤0.025 |
| S | ≤0.025 |
| Si | 0.3-0.5 |
| Ni | 0.8-1.0 |
| Cr | ≤0.30 |
| Mo | ≤0.25 |
| Cu | 1.25-1.50 |
| Nb | 0.02-0.06 |
| Ti | 0.01-0.03 |
| Thickness mm | Yield StrengthMin Mpa | Tensile Strength Min Mpa | Elongation Min % |
| 5t≤50 | 485 | 550 | 20 |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Size | As Per Requirement |
| Usage/Application | Industrial |
| Certification | ISO |
| I Deal In | New Only |
| Packing Details | Shrink Wrapping, Jute Wrapping, Bubble Wrapping, Wooden Boxes or As Per Requirement |
| Element | % |
| C | 0.12-0.20 |
| Mn | 0.40-0.70 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.20-0.40 |
| Ni | - |
| Cr | 1.40-2.00 |
| Mo | 0.40-0.60 |
| V | - |
| Ti | 0.01-0.10 |
| Zr | - |
| Cu | 0.15-0.50 |
| B | 0.001-0.005 |
| Nb | - |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 20 | 690 | 760-895 | 18 |
| 20-65 | 690 | 760-895 | 18 |
| 65-150 | 620 | 690-895 | 18 |
| Brand | Aesteiron |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm |
| Material Grade | 316 |
| Standard | ASTM |
| Surface Treatment | Coated, Hot Rolled |
| Steel Grade | SS 304, SS316 L, SS304 L |
Aesteiron Steels LLP is one of the leading manufacturers & suppliers of ASTM A240 Grade 316Ti Sheet Plate.
We are offering:
ASTM A240 Grade 316Ti Sheet Stockist
ASTM A240 Grade 316Ti Sheet Suppliers
ASTM A240 Grade 316Ti Sheet Traders
ASTM A240 Grade 316Ti Sheet Dealers
ASTM A240 Grade 316Ti Sheet Manufacturers
ASTM A240 Grade 316Ti Sheet Exporters
ASTM A240 Grade 316Ti Plate Stockist
ASTM A240 Grade 316Ti Plate Suppliers
ASTM A240 Grade 316Ti Plate Traders
ASTM A240 Grade 316Ti Plate Dealers
ASTM A240 Grade 316Ti Plate Manufacturers
ASTM A240 Grade 316Ti Plate Exporters
Grades under ASTM A240 Sheet
ASTM A240 Grade 800 Sheet Plate
ASTM A240 Grade 800H Sheet Plate
ASTM A240 Grade 904L Sheet Plate
ASTM A240 Grade 201 Sheet Plate
ASTM A240 Grade 202 Sheet Plate
ASTM A240 Grade XM-19 Sheet Plate
ASTM A240 Grade XM-31 Sheet Plate
ASTM A240 Grade XM-17 Sheet Plate
ASTM A240 Grade XM-18 Sheet Plate
ASTM A240 Grade XM-29 Sheet Plate
ASTM A240 Grade 301 Sheet Plate
ASTM A240 Grade 301L Sheet Plate
ASTM A240 Grade 301LN Sheet Plate
ASTM A240 Grade 302 Sheet Plate
ASTM A240 Grade 304 Sheet Plate
ASTM A240 Grade 304L Sheet Plate
ASTM A240 Grade 304H Sheet Plate
ASTM A240 Grade 304N Sheet Plate
ASTM A240 Grade XM-21 Sheet Plate
ASTM A240 Grade 305 Sheet Plate
ASTM A240 Grade 309S Sheet Plate
ASTM A240 Grade 309H Sheet Plate
ASTM A240 Grade 309Cb Sheet Plate
ASTM A240 Grade 309HCb Sheet Plate
ASTM A240 Grade 310S Sheet Plate
ASTM A240 Grade 310H Sheet Plate
ASTM A240 Grade 310Cb Sheet Plate
ASTM A240 Grade 310HCb Sheet Plate
ASTM A240 Grade 310 MoLN Sheet Plate
ASTM A240 Grade 316 Sheet Plate
ASTM A240 Grade 316L Sheet Plate
ASTM A240 Grade 316H Sheet Plate
ASTM A240 Grade 316Ti Sheet Plate
ASTM A240 Grade 316Cb Sheet Plate
ASTM A240 Grade 316N Sheet Plate
ASTM A240 Grade 316LN Sheet Plate
ASTM A240 Grade 317 Sheet Plate
ASTM A240 Grade 317L Sheet Plate
ASTM A240 Grade 317LM Sheet Plate
ASTM A240 Grade 317LMN Sheet Plate
ASTM A240 Grade 317LN Sheet Plate
ASTM A240 Grade 321 Sheet Plate
ASTM A240 Grade 321H Sheet Plate
ASTM A240 Grade 334 Sheet Plate
ASTM A240 Grade 347 Sheet Plate
ASTM A240 Grade 347H Sheet Plate
ASTM A240 Grade 348 Sheet Plate
ASTM A240 Grade 348H Sheet Plate
ASTM A240 Grade XM-15 Sheet Plate
Chemical Composition
|
Element |
% |
|
Carbon |
0.08 |
|
Manganese |
2.00 |
|
Phosphorus |
0.045 |
|
Sulfur |
0.030 |
|
Silicon |
0.75 |
|
Chromium |
16.0-18.0 |
|
Nickel |
10.0-14.0 |
|
Molybdenum |
2.00-3.00 |
|
Nitrogen |
0.10 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm |
| Steel Grade | SS316 L, SS304 L, SS409 L, SS200 |
| Surface Treatment | Painted, Hot Rolled, Cold Rolled |
| Type | Plate |
| Element | % |
| Carbon | 0.030 |
| Manganese | 2.00 |
| Phosphorus | 0.045 |
| Sulfur | 0.030 |
| Silicon | 0.75 |
| Chromium | 18.0-20.0 |
| Nickel | 13.5-17.5 |
| Molybdenum | 4.00-5.00 |
| Nitrogen | 0.20 |
| Brand | Aesteiron |
| Size (feet X feet) | 4 x 6 |
| Thickness | 1-2 mm, 2-3 mm, 3-4 mm |
| Material Grade | A 240 |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Standard | ASTM, AISI, JIS, DIN |
| Steel Grade | SS 304, SS316 L, SS304 L, SS200 |
| Certification | ROHS, SGS, IBR, ISO |
| Element | % |
| C max | 0.18 |
| Si max | 0.5 |
| Mn | 0.90-1.60 |
| P max | 0.035 |
| S max | 0.035 |
| Als min | 0.015 |
| Ti max | 0.02 |
| Cu max | 0.35 |
| Cr max | 0.2 |
| Ni max | 0.4 |
| Mo max | 0.08 |
Grade | Rm | Re(MPa) min | A% min | Akv/J min | ||||||
ASTM A131 GRADE DH32 | 440-570 | 315 | 22 | E.T °C | Thickness (mm) | |||||
-20 | ≤ 50 | >50-70 | >70-100 | |||||||
L | C | L | C | L | C | |||||
31 | 22 | 38 | 26 | 46 | 31 | |||||
*Your information is safe with us.
| Brand | Aesteiron |
| Size (feet X feet) | 4 x 6 |
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm |
| Material Grade | 321 |
| Element | % |
| Carbon | 0.04-0.10 |
| Manganese | 2.00 |
| Phosphorus | 0.045 |
| Sulfur | 0.030 |
| Silicon | 0.75 |
| Chromium | 17.0-19.0 |
| Nickel | 9.0-12.0 |
| Grade | ASTM A514 Grade B |
| Surface Treatment | Hot Rolled |
| Thickness | Upto 40 cm,2-3 mm,3-4 mm |
| Material Grade | ASTM 514 |
| Element | % |
| C | 0.12-0.21 |
| Mn | 0.7-1.00 |
| P | 0.035 |
| S | 0.008 |
| Si | 0.20-0.35 |
| Ni | - |
| Cr | 0.4-0.65 |
| Mo | 0.15-0.25 |
| V | 0.03-0.08 |
| Ti | 0.01-0.04 |
| Zr | - |
| Cu | - |
| B | 0.0025 |
| Thickness (mm) | Tensile strength .ksi [MPa] | Yield strength Min ksi [MPa] | Elongation in under 50mm,min by % | Hardness HBW |
| - | 110-130 ksi | 100 ksi, min | 16 in 2 inch | 235-293 |
| Thickness | 2-3 mm, >5 mm, 3-4 mm, 4-5 mm, 1-2 mm, 0-1 mm |
| Element | % |
| C | 0.21 |
| Si | 0.50 |
| Mn(min) | 2.5*C |
| P | 0.035 |
| S | 0.035 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C max | 0.18 |
| Si max | 0.5 |
| Mn | 0.90-1.60 |
| P max | 0.035 |
| S max | 0.035 |
| Als min | 0.015 |
| Ti max | 0.02 |
| Cu max | 0.35 |
| Cr max | 0.2 |
| Ni max | 0.4 |
| Mo max | 0.08 |
| Grade | Rm | Re(MPa) min | A% min | Akv/J min | ||||||
| (MPa) | ||||||||||
| AH32 | 440-570 | 315 | 22 | E.T °C | Thickness (mm) | |||||
| 0 | ≤ 50 | >50-70 | >70-100 | |||||||
| L | C | L | C | L | C | |||||
| 31 | 22 | 38 | 26 | 46 | 31 | |||||
| Thickness | 2-3 mm, 3-4 mm, >5 mm, 1-2 mm, 0-1 mm, 4-5 mm |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Element | % |
| C | 0.18 |
| Si | 0.50 |
| Mn | 0.9/1.60 |
| P | 0.035 |
| S | 0.035 |
| Al acid | ≥ 0.015 |
| Nb | 0.02/0.05 |
| V | 0.03/0.10 |
| Ti | 0.02 |
| Ni | 0.40 |
| Cu | 0.35 |
| Cr | 0.20 |
| Mo | 0.08 |
| N | - |
| Yield strength (Mpa) | Tensile strength (Mpa) | Impacting Test |
| temperature (℃) | ||
| ≥390 | 510-650 | 0 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.21 |
| Si | 0.10/0.35 |
| Mn | 0.6 |
| P | 0.035 |
| S | 0.035 |
| Al(acid) | 0.035 |
| Yield strength (Mpa) | Tensile strength (Mpa) | Impacting Test |
| temperature (℃) | ||
| ≥235 | 400-520 | -20 |
*Your information is safe with us.
| Grade | ASTM A131 Grade FH36 |
| Element | % |
| C max | 0.16 |
| Si max | 0.5 |
| Mn | 0.90-1.60 |
| P max | 0.025 |
| S max | 0.025 |
| Als min | 0.015 |
| Ti max | 0.02 |
| Cu max | 0.35 |
| Cr max | 0.2 |
| Ni max | 0.8 |
| Mo max | 0.08 |
| Nb | 0.02-0.05 |
| V | 0.05-0.10 |
| N max | 0.009 |
| Grade | Rm | Re(MPa) min | A% min | Akv/J min | ||||||
| (MPa) | ||||||||||
| ASTM A131 GRADE FH36 Plates | 490-630 | 355 | 21 | E.T °C | Thickness (mm) | |||||
| -60 | ≤ 50 | >50-70 | >70-100 | |||||||
| L | C | L | C | L | C | |||||
| 34 | 24 | - | - | - | - | |||||
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.17-0.23 |
| Si | 0.13-0.45 |
| Mn | 0.78-0.88 |
| P | 0.035 |
| S | 0.035 |
| Ni | 2.03-2.57 |
| N | - |
| Thickness mm | Yield Strength Min Mpa | Tensile Strength Mpa | Elongation Min % |
| 5≤t≤50 | 255 | 450-585 | 19% |
| 50≤t≤200 | 255 | 450-585 | 15% |
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Element | % |
| C | 0.05-0.21 |
| Mn | 0.55-0.80 |
| P | 0.025 |
| S | 0.025 |
| Si | 0.15-0.40 |
| Cr | 0.50-0.80 |
| Mo | 0.45-0.60 |
| V | - |
| Tensile (MPa) | Yield (MPa) | Elong. (50 mm) |
| 485 - 620 | 310 min | 22% min |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.28-0.33 |
| Mn | 0.98 |
| P | 0.035 |
| S | 0.035 |
| Si | 0.13-0.45 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 200 | 240 | 450-585 | 19 |
| 50 | 23 |
| Thickness | 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm |
| Element | % |
| C | 0.24-0.29 |
| Si | 0.13-0.45 |
| Mn | 0.79-1.30 |
| P | 0.035 |
| S | 0.035 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 6-40 | 240 | 450-585 | 23% |
| 40-100 | 240 | 450-585 | 19% |
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.23 |
| Cr | 1.5 - 2.0 |
| Fe | 94.29 |
| Mn | 0.40 |
| Ni | 2.6 - 3.25 |
| P | 0.035 |
| Si | 0.20 - 0.40 |
| S | 0 |
| V | 0.030 |
*Your information is safe with us.
| Steel Grade | SS 304, SS316 L, SS304 L |
| Standard | ASTM |
| Surface Treatment | Hot Rolled |
| Element | % |
| C | 0.03-0.09 |
| Mn | 0.45-1.3 |
| P | ≤0.025 |
| S | ≤0.025 |
| Si | 0.3-0.5 |
| Ni | 0.8-1.0 |
| Cr | ≤0.30 |
| Mo | ≤0.25 |
| Cu | 1.25-1.50 |
| Nb | 0.02-0.06 |
| Ti | 0.01-0.03 |
| Thickness mm | Yield Strength Min Mpa | Tensile Strength Min Mpa | Elongation Min % |
| 5t≤20 | 515 | 585 | 20 |
| 20t≤50 | 485 | 550 | 20 |
| Nickel Grades | 20, 22, 36, 41, 188, 200, 201, 400, 600, 601, 617, 625, 718, 800/800H/800HT, 825, |
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.21 |
| Si | 0.5 |
| Mn | Min. 2.5*C |
| P | 0.035 |
| S | 0.035 |
| Yield strength (Mpa) | Tensile strength (Mpa) | Impacting Test temperature (℃) |
| ≥235 | 400-520 | 20 |
*Your information is safe with us.
| Thickness | >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Element | % |
| C | 0.18 |
| Si | 0.10/0.50 |
| Mn (min) | 0.90/1.60 |
| P | 0.035 |
| S | 0.035 |
| Al | 0.015 |
| Nb | 0.02-0.05 |
| V | 0.05-0.10 |
| Ti | 0.02 |
| Cb | 0.02/0.05 |
| V | 0.05/0.10 |
| Cu | 0.35 |
| Cr | 0.2 |
| Ni | 0.4 |
| Mo | 0.08 |
| Standard | ASTM |
| Thickness | 4-5 mm, >5 mm, 2-3 mm, 0-1 mm, 1-2 mm, 3-4 mm |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Element | % |
| C | 0.21 |
| Si | 0.10-0.35 |
| Mn | 0.70 |
| P | 0.035 |
| S | 0.035 |
| C Mn/6 | 0.40 |
ASTM A131 Grade E shipbuilding steel plate
is mainly used to shipbuilding project and ocean offshore structural project.
| Thickness | 1-2 mm,2-3 mm,3-4 mm,>5 mm, 4-5 mm, 0-1 mm |
| Element | % |
| C | 0.18 |
| Si | 0.10/0.50 |
| Mn (min) | 0.90/1.60 |
| P | 0.035 |
| S | 0.035 |
| Cr | 0.2 |
| Mo | 0.08 |
| Ni | 0.4 |
| Cu | 0.35 |
| Cb | 0.02/0.05 |
| V | 0.05/0.10 |
| Yield strength (Mpa) | Tensile strength (Mpa) | Impacting Test |
| temperature (℃) | ||
| ≥355 | 490-620 | -40 |
*Your information is safe with us.
| Thickness | 3-4 mm, 4-5 mm, >5 mm, 2-3 mm, 0-1 mm, 1-2 mm |
| Surface Treatment | Coated, Painted, Hot Rolled |
| Standard | ASTM |
Aesteiron Steels Pvt Ltd is one of the leading manufacturers, suppliers and exporters of ASTM A131 Grade EH32 Plate.
We are:
ASTM A131 Grade EH32 Plate Stockist
ASTM A131 Grade EH32 Plate Supplier
ASTM A131 Grade EH32 Plate Trader
ASTM A131 Grade EH32 Plate Exporter
ASTM A131 Grade EH32 Plate Manufacturer
ASTM A131 Grade EH32 Plate Exporter
ASTM A131 Grade EH32 forms:-
ASTM A131 Grade EH32 Plate
ASME SA131 Grade EH32 Plate
ASTM A131 Gr EH32 Plate
ASME SA131 Gr EH32 Plate
ASTM A131 Grade EH32 Sheet
ASME SA131 Grade EH32 Sheet
ASTM A131 Gr EH32 Sheet
ASME SA131 Gr EH32 Sheet
ASTM A131 Grade EH32 Chemical Composition
Element | % |
C | 0.18 |
Si | 0.1-0.50 |
Mn | 0.90-1.6 |
P | 0.035 |
| 0.035 |
Al | 0.015 |
Nb | 0.02-0.05 |
V | 0.05-0.10 |
Ti | 0.02 |
Cu | 0.35 |
Cr | 0.2 |
Ni | 0.4 |
Mo | 0.08 |
ASTM A131 Grade EH32 Mechanical Properties
Yield strength (Mpa) | Tensile strength (Mpa) | Steel Mark |
315 | 440-590 | A131/EH32 |
Please contact us for more details.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.18 |
| Si | 0.10/0.50 |
| Mn(min) | 0.90/1.60 |
| P | 0.035 |
| S | 0.035 |
| Cr | 0.2 |
| Mo | 0.08 |
| Ni | 0.4 |
| Cu | 0.35 |
| Cb | 0.02/0.05 |
| V | 0.05/0.10 |
| Grade | Re | Rm | Elongation | |
| A50mm | A200mm | |||
| MPa | MPa | % | % | |
| DH40 | 355 | 490/620 | 22 | 19 |
| Thickness | 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm |
| Element | % |
| C | 0.16 |
| Si | 0.10-0.5 |
| Mn | 0.9-1.6 |
| P | 0.025 |
| S | 0.025 |
| V | 0.05-0.10 |
| Al | 0.015 |
| Cr | 0.2 |
| Cu | 0.35 |
| Mo | 0.08 |
| Nb | 0.02-0.05 |
| Ni | 0.08 |
| Ti | 0.02 |
| N | 0.012 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.17 |
| Si | 0.13-0.45 |
| Mn | 0.78-0.88 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 70-90[485-620] |
| Yield strength, min, kis [MPa] | 40 [275] |
| Elongation in 8 in. [200 mm], min, % | 17 |
| Elongation in 2 in. [50 mm], min, % | 21 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.2 |
| Si | 0.13-0.45 |
| Mn | 0.70-0.80 |
| P | 0.035 |
| S | 0.035 |
| Tensile strength, kis [MPa] | 80-100 [485-620] |
| Yield strength, min, kis [MPa] | 55 [380] |
| Elongation in 8 in. [200 mm], min, % | … |
| Elongation in 2 in. [50 mm], min, % | 20 |
| Grade | ASTM A387 Grade 9 |
| Element | % |
| C | 0.15 |
| Mn | 0.30-0.60 |
| P | 0.025 |
| S | 0.025 |
| Si | 1.00 |
| Cr | 8.00-10.00 |
| Mo | 0.90-1.10 |
| V | 0.04 |
| Tensile (MPa) | Yield (MPa) | Elong. (50mm) |
| 415 - 585 | 205 min | 18% min |
*Your information is safe with us.
| Thickness | 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm |
| Element | % |
| C | 0.18 |
| Si | 0.4 |
| Mn | 0.95/1.50 |
| P | 0.015 |
| S | 0.008 |
| Al | 0.02 (Min) |
| Cr | 0.3 |
| Cu | 0.3 |
| Ni | 0.3 |
| Mo | 0.08 |
| Nb | 0.01 |
| Ti | 0.03 |
| V | 0.02 |
| Properties | Value |
| Tensile strength (N/mm2) | 415/580 |
| Yield stress/ min (N/mm2) | 265 |
| Thickness | 2-3 mm, 0-1 mm, 4-5 mm, >5 mm, 3-4 mm, 1-2 mm |
| Element | % |
| C | 0.13-0.23 |
| Si | 0.13-0.37 |
| Mn | 0.64-1.10 |
| P | 0.035 |
| S | 0.035 |
| Cr | 0.36-0.69 |
| Mo | 0.12-0.28 |
| B | 0.0005-0.005 |
| Ti | 0.01-0.05 |
| V | 0.02-0.09 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 06-65 | 690 | 795-930 | 16% |
| 65-150 | 620 | 725-930 | 14% |
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.11 Max |
| Mn | 1.10 - 1.35 |
| P | 0.020 Max |
| S | 0.006 Max. |
| Si | 0.30 - 0.50 |
| Cu | 0.25 - 0.40 |
| Ni | 0.25 - 0.40 |
| Cr | 0.45 - 0.70 |
| Mo | 0.02 - 0.08 |
| V | 0.04 - 0.08 |
| Al | 0.01 - 0.04 |
| Ni | 0.015 Max |
| Yield strength (min) | 70 ksi (345 Mpa) |
| Tensile strength | 85-110 ksi (585-760 Mpa) |
| Elongation in 2" (50 mm)min | 19% |
*Your information is safe with us.
| Grade | ASTM A710 Grade B |
| Element | % |
| C | 0.03-0.09 |
| Mn | 0.45-1.3 |
| P | ≤0.025 |
| S | ≤0.025 |
| Si | 0.3-0.5 |
| Ni | 0.8-1.0 |
| Cr | ≤0.30 |
| Mo | ≤0.25 |
| Cu | 1.25-1.50 |
| Nb | 0.02-0.06 |
| Ti | 0.01-0.03 |
| Thickness mm | Yield StrengthMin Mpa | Tensile Strength Min Mpa | Elongation Min % |
| 5t≤50 | 485 | 550 | 20 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| C | 0.18 |
| Mn | 1.00-1.60 |
| P | 0.035 |
| S | 0.04 |
| Si | 0.55 |
| Cr | 0.25 |
| Ni | 0.25 (max) |
| Mo | 0.08 (max) |
| V | 0.08 (max) |
| Cu | 0.35 (max) |
| Density (×1000 kg/m3) | 7.7-8.03 |
| Poisson's Ratio | 0.27-0.30 |
| Elastic Modulus (GPa) | 190-210 |
| Thickness | 3-4 mm, 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm |
| Element | % |
| C | 0.17 |
| Mn | 0.45-0.75 |
| P | 0.035 |
| S | 0.015 |
| Si | 0.35 |
| Cr | 0.90-1.20 |
| Ni | 0.90-1.20 |
| Mo | 0.25-0.40 |
| Al | 0.06 |
| Properties | |
| Density (×1000 kg/m3) | 7.7-8.03 |
| Poisson's Ratio | 0.27-0.30 |
| Elastic Modulus (GPa) | 190-210 |
*Your information is safe with us.
| Thickness | 4-5 mm, 2-3 mm, 0-1 mm, 1-2 mm, >5 mm, 3-4 mm |
| Element | (%) |
| C | 0.360 - 0.440 |
| Mn | 1.35 - 1.65 |
| S | 0.05 |
| P | 0.04 |
| Fe | 97.82 - 98.29 |
| Properties | Metric | Imperial |
| Density | 7.7-8.03 g/cm3 | 0.278-0.290 lb/in3 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | 0.15 |
| Si | 0.15-0.50 |
| Mn | 0.70-1.60 |
| P | 0.03 |
| S | 0.025 |
| Cu | ≤0.35 |
| Ni | ≤0.60 |
| Cr | ≤0.25 |
| Mo | ≤0.30 |
| V | ≤0.06 |
| Co | ≤0.03 |
| Thickness | 0-1 mm, 1-2 mm, >5 mm, 3-4 mm, 4-5 mm, 2-3 mm |
| Element | % |
| C | ≤0.10 |
| Mn | 1.1-1.65 |
| P | ≤0.025 |
| S | ≤0.01 |
| Si | 0.1-0.50 |
| Ni | ≤0.40 |
| Cr | ≤0.20 |
| Mo | ≤0.06 |
| Cu | ≤0.35 |
| V | ≤0.10 |
| Nb | ≤0.05 |
| Al | ≤0.08 |
| Thickness | Yield | Tensile | Elongation |
| Strength | Strength | ||
| mm | Min Mpa | Mpa | Min % |
| 5t≤300 | 345 | 485-620 | 21 |
*Your information is safe with us.
| Thickness | 0-1 mm, 1-2 mm, 2-3 mm, 3-4 mm, 4-5 mm, >5 mm |
| Element | % |
| C | 0.2 |
| Si | 0.15-0.50 |
| Mn | 0.70-1.60 |
| P | 0.03 |
| S | 0.03 |
| Cu | ≤0.35 |
| Ni | ≤0.25 |
| Cr | ≤0.25 |
| Mo | ≤0.08 |
| V | ≤0.06 |
| Co | ≤0.03 |
| Thickness mm | Yield Min Mpa | Tensile Mpa | Elongation Min % |
| 5-40 | 345 | 480-620 | 22% |
| 40-65 | 345 | 480-620 | 22% |
| 65 | 310 | 450-585 | 22% |